Effect of Counterface Material on Friction and Wear Behavior of Ni-Cr-W-Al-Ti-MoS_2 Composites

Ni-Cr-W-Al-Ti-MoS2 self-lubricating composites were prepared through the powder metallurgy (P/M) method. Their friction properties were investigated by a pin-on-disk tribometer in the range from the room temperature to 600 ℃. Alumina, silicon nitride and nickel-iron-sulfide alloys were selected as the counterface materials. Results indicate that the lowest friction coefficients under 0.22 can be obtained at 600 ℃ when rubbed against alumina. When rubbed against nickel-iron-sulfide alloys, are presented the lowest wear rates in the magnitude of 10-6 mm3/N·m, one order of magnitude lower than those when rubbed against ceramics. In the case of three rubbing pairs, the wear rates of the composite containing MoS2 present themselves inversely proportional to friction coefficients. With alumina ceramics used as a counterface, transfer films and glaze layers will form on the contact surface playing a main role in lubrication at high temperatures. However, when silicon nitride and nickel-iron-sulfide alloy are used, the lubricating transfer films appear not to be promi-nent.     

NiCoP合金包覆空心微珠粉体的制备

采用粉体化学镀技术，以AgNO3取代常见的贵金属盐PdCl2作为活化剂，H2PO2^-取代Sn^2 作为还原剂，在空心微珠表面包覆NiCoP合金。利用扫描电镜、能谱分析仪分析包覆层的形貌和成分。结果表明NiCoP合金均匀包覆在空心微珠表面。并提出了这种改进工艺的一种可能的机理。     

某飞机系列粉末合金刹车盘改进技术的研究

通过改进整盘钢骨架两面烧结粉末合金刹车盘的结构,直接成形卸荷槽,取消冲卸荷槽工序,完全解决该刹车盘长期存在的在后续加工及使用过程中的掉块问题。     

P／MRene＇95合金缓冷处理与等温变形研究

本文对Ｐ／ＭＲｅｎｅ＇９５合金缓冷处理与等温变形进行了研究，探索采用缓冷处理降低合金等温变形时流变应力的可行性，煅造出φ２２０ｍｍ的涡轮盘试件。结果表明：缓冷处理改变了合金中γ＇相的尺寸和分布，对合金流变应力具有显著的影响，可促进等温变形时动态回复和动态再结晶的发生，细化晶粒。φ２２０ｍｍ涡轮盘的力学性能达到了技术规范的要求。     

粉末冶金γ-TiAl基合金研究的最新进展

γ TiAl基合金是一种具有发展前途的新一代高温结构材料。首先综述了γ TiAl基合金的性能特点和应用前景 ,并简单介绍了该合金的最新基础研究情况。随后介绍了采用粉末冶金方法制备γ TiAl基合金的基本工艺、力学性能 ,最后结合γ TiAl基合金排气阀和板材的研制论述了粉末冶金在γ TiAl基合金制备及近净成形方面的优势和发展前景     

填加造孔剂法制备泡沫铝及其吸能性能

以尿素为造孔剂,采用填加造孔剂法制备泡沫铝,系统研究了成型烧结温度、孔隙率和孔径大小对泡沫铝吸能性能的影响,在此过程中采用电子万能试验机和数字图像相关(DIC)技术同步测试分析。结果表明:填加造孔剂法可以良好的控制泡沫铝的孔隙率和孔径;泡沫铝的最佳成型烧结温度为650℃,在此温度下,泡沫铝的压缩屈服强度达到10.7 MPa;随着孔隙率的降低,泡沫铝的屈服强度和平台应力逐渐提高,材料吸能性能有显著增强;当孔径小于2.0 mm时,随着孔径的增大,材料的吸能性能小幅提高。DIC技术可以直观的表征泡沫材料力学行为,具有良好的工程应用前景。     

Single track and single layer formation in selective laser melting of niobium solid solution alloy

Selective laser melting (SLM) was employed to fabricate Nb-37Ti-13Cr-2Al-1Si (at%) alloy, using pre-alloyed powders prepared by plasma rotating electrode processing (PREP). A series of single tracks and single layers under different processing parameters was manufactured to evaluate the processing feasibility by SLM, including laser power, scanning speed, and hatch distance. Results showed that continuous single tracks could be fabricated using proper laser powers and scanning velocities. Both the width of a single track and its penetration depth into a substrate increased with an increase of the linear laser beam energy density (LED), i.e., an increase of the laser power and a decrease of the scanning speed. Nb, Ti, Si, Cr, and Al elements distributed heterogeneously over the melt pool in the form of swirl-like patterns. An excess of the hatch distance was not able to interconnect neighboring tracks. Under improper processing parameters, a balling phenomenon occurred, but could be eliminated with an increased LED. This work testified the SLM-processing feasibility of Nb-based alloy and promoted the application of SLM to the manufacture of niobium-based alloys.     

送粉方式对等离子喷涂NiCrAlY/ Al2 O3涂层介电性能的影响

以内送粉和外送粉两种方式微弧等离子喷涂工艺制备了NiCrAlY/Al_2O_3复合涂层,分析了送粉方式对涂层相组成、微观结构和介电性能的影响。结果表明:与外送粉相比,内送粉方式沉积的涂层具有较高的沉积效率和较低的孔隙率。由于喷涂过程中α-Al_2O_3颗粒完全熔融,内送粉喷涂所得到涂层主要为γ/γ′和γ-Al_2O_3相,并且涂层结构致密,NiCrAlY颗粒分布均匀。介电性能测试表明,以外送粉方式制备的涂层复介电常数实部和虚部几乎不随频率发生变化。而以内送粉方式喷涂的涂层复介电常数实部和虚部随频率的增加而降低,呈现明显的频散现象。     

粉煤灰颗粒增强铝基复合材料的耐磨性研究

以粒度为80μm的粉煤灰为增强相,粒度为30μm的铝粉为基体,采用粉末冶金法成功制备了粉煤灰颗粒增强铝基复合材料。经SEM、金相显微镜等分析手段对制备的复合材料进行组织观察,并对其进行耐磨性测试。结果表明,粉煤灰含量为20%,烧结温度为650℃时,相对损率最小为0.1590%。随着粉煤灰含量和保压时间的增加,试样的耐磨性逐渐升高,随着烧结温度升高,试样的耐磨性呈现出先升高后降低的趋势。     

基于应力循环特征的裂纹萌生寿命预测方法

以两种镍基高温合金的应力循环特征为基础,即粉末高温合金FGH95的循环硬化继而软化及变形高温合金GH4169的循环软化特性,寻求载荷历程相关的损伤参量,进而建立应力弱化损伤模型,以考虑载荷历程对疲劳寿命的影响.建立的应力弱化损伤模型可以较好地预测不同循环载荷条件下的疲劳寿命,其预测精度不低于传统方法,且优势在于使建立模型所需要的试样数量大大减少.